T1 - (Ferrocenylpyrazolyl)zinc(II) benzoates as catalysts for the ring opening polymerization of ε-caprolactone
AU - Obuah, Collins
AU - Lochee, Yemanlall
AU - Jordaan, Johan H.L.
AU - Otto, Daniel P.
AU - Nyokong, Tebello
AU - Darkwa, James
N1 - Publisher Copyright:
© 2015 Elsevier Ltd. All rights reserved.
PY - 2015/4/18
Y1 - 2015/4/18
N2 - The reaction of Zn(OAc)2 and C6H5COOH or 3,5-NO2-C6H3COOH with 3-ferrocenylpyrazolyl-methylenepyridine (L1), 3-ferrocenyl-5-methylpyrazolyl-methylenepyridine (L2), 3-ferrocenylpyrazolyl-ethylamine (L3) and 3-ferrocenyl-5-pyrazolyl-ethylamine (L4) afford the corresponding complexes [Zn(C6H5COO)2(L1)] (1), [Zn(C6H5COO)2(L2)] (2), [Zn(3,5-NO2-C6H3COO)2(L1)] (3), [Zn(3,5-NO2-C6H3COO)2(L2)] (4), [Zn(C6H5COO)2(L3)] (5), [Zn(C6H5COO)2(L4)] (6), [Zn(3,5-NO2-C6H3COO)2(L3)] (7) and [Zn(3,5-NO2-C6H3COO)2(L4)] (8). These complexes behave as catalysts for the ring opening polymerization of ε-caprolactone to produce polymers with molecular weight that range from 1480 to 7080 g mol-1 and exhibited moderate to broad PDIs. Evidence of these complexes acting as catalysts was obtained from both the polymerization data and kinetic studies. The polymerization data show that variation of the [CL]/[C] from 100 to 800 produced PCL with relatively the same molecular weight indicative of a catalyst behavior. The appearance of induction period in kinetic plots strengthens the fact that these complexes are catalysts rather than initiators. MALDI-TOF MS and 1H NMR data show di-hydroxy end groups, which support the coordination mechanism rather than insertion mechanism. To understand the broad PDIs obtained for some of the polymer, the electronic properties of the zinc complexes were investigated using cyclic voltammetry. The results show that the zinc complexes containing amine based ligands are highly electrophilic therefore making them unstable, hence the broad PDIs observed for zinc complexes containing amine based ligands. Among the eight complexes investigated, complex 7 is the most active catalyst with kp value of 1.18 × 10-7 h-1 mol-1 at 110 °C.
AB - The reaction of Zn(OAc)2 and C6H5COOH or 3,5-NO2-C6H3COOH with 3-ferrocenylpyrazolyl-methylenepyridine (L1), 3-ferrocenyl-5-methylpyrazolyl-methylenepyridine (L2), 3-ferrocenylpyrazolyl-ethylamine (L3) and 3-ferrocenyl-5-pyrazolyl-ethylamine (L4) afford the corresponding complexes [Zn(C6H5COO)2(L1)] (1), [Zn(C6H5COO)2(L2)] (2), [Zn(3,5-NO2-C6H3COO)2(L1)] (3), [Zn(3,5-NO2-C6H3COO)2(L2)] (4), [Zn(C6H5COO)2(L3)] (5), [Zn(C6H5COO)2(L4)] (6), [Zn(3,5-NO2-C6H3COO)2(L3)] (7) and [Zn(3,5-NO2-C6H3COO)2(L4)] (8). These complexes behave as catalysts for the ring opening polymerization of ε-caprolactone to produce polymers with molecular weight that range from 1480 to 7080 g mol-1 and exhibited moderate to broad PDIs. Evidence of these complexes acting as catalysts was obtained from both the polymerization data and kinetic studies. The polymerization data show that variation of the [CL]/[C] from 100 to 800 produced PCL with relatively the same molecular weight indicative of a catalyst behavior. The appearance of induction period in kinetic plots strengthens the fact that these complexes are catalysts rather than initiators. MALDI-TOF MS and 1H NMR data show di-hydroxy end groups, which support the coordination mechanism rather than insertion mechanism. To understand the broad PDIs obtained for some of the polymer, the electronic properties of the zinc complexes were investigated using cyclic voltammetry. The results show that the zinc complexes containing amine based ligands are highly electrophilic therefore making them unstable, hence the broad PDIs observed for zinc complexes containing amine based ligands. Among the eight complexes investigated, complex 7 is the most active catalyst with kp value of 1.18 × 10-7 h-1 mol-1 at 110 °C.
KW - (Ferrocenylpyrazolyl)zinc(II) benzoates
KW - Catalysts
KW - Electrophilicity
KW - Ring opening polymerization
KW - ε-Caprolactone
UR - http://www.scopus.com/inward/record.url?scp=84923864369&partnerID=8YFLogxK
U2 - 10.1016/j.poly.2015.02.007
DO - 10.1016/j.poly.2015.02.007
M3 - Article
AN - SCOPUS:84923864369
SN - 0277-5387
VL - 90
SP - 154
EP - 164
JO - Polyhedron
JF - Polyhedron
ER -