TY - JOUR
T1 - Boric acid production from colemanite together with ex situ CO2 sequestration
AU - Gönen, Mehmet
AU - Nyankson, Emmanuel
AU - Gupta, Ram B.
N1 - Publisher Copyright:
© 2016 American Chemical Society.
PY - 2016/5/4
Y1 - 2016/5/4
N2 - In this work, boric acid (H3BO3) production from the mineral colemanite (Ca2B6O11·5H2O) with carbon dioxide (CO2) sequestration is investigated. CO2, a known greenhouse gas, is used as a raw material in the leaching of boric acid from colemanite, and the residual calcium is converted into the thermodynamically stable carbonate form. Experiments are carried out in a high pressure stainless steel reactor equipped with stirring and ultrasonic mixing. The solid/ liquid ratio is kept at 0.1 g/mL considering the solubility of boric acid extracted, and two different particle sizes (45 and 75 μm) of colemanite are tested. Reactions were carried out for different reaction times and at 40-70 °C and at 4-12 MPa. Characterization of the products by FTIR, XRD, and TGA confirmed that boric acid is extracted from colemanite and CO2 is converted into calcium carbonate. The conversion favorably increases with the addition of CO2 pressure up to 8 MPa. The use of 20-25 kHz ultrasound in this heterogeneous reaction increased the extraction efficiency from approximately 70% to 90% due to enhanced mass transfer. CO2 storage capacity of colemanite is measured as 0.17 as compared to the theoretical value of 0.21 kg CO2/kg mineral. The utilization of CO2 in boric acid production can sequester a significant amount of CO2 while improving the environmental performance as compared to traditional sulfuric acid-based processes.
AB - In this work, boric acid (H3BO3) production from the mineral colemanite (Ca2B6O11·5H2O) with carbon dioxide (CO2) sequestration is investigated. CO2, a known greenhouse gas, is used as a raw material in the leaching of boric acid from colemanite, and the residual calcium is converted into the thermodynamically stable carbonate form. Experiments are carried out in a high pressure stainless steel reactor equipped with stirring and ultrasonic mixing. The solid/ liquid ratio is kept at 0.1 g/mL considering the solubility of boric acid extracted, and two different particle sizes (45 and 75 μm) of colemanite are tested. Reactions were carried out for different reaction times and at 40-70 °C and at 4-12 MPa. Characterization of the products by FTIR, XRD, and TGA confirmed that boric acid is extracted from colemanite and CO2 is converted into calcium carbonate. The conversion favorably increases with the addition of CO2 pressure up to 8 MPa. The use of 20-25 kHz ultrasound in this heterogeneous reaction increased the extraction efficiency from approximately 70% to 90% due to enhanced mass transfer. CO2 storage capacity of colemanite is measured as 0.17 as compared to the theoretical value of 0.21 kg CO2/kg mineral. The utilization of CO2 in boric acid production can sequester a significant amount of CO2 while improving the environmental performance as compared to traditional sulfuric acid-based processes.
UR - http://www.scopus.com/inward/record.url?scp=84968791875&partnerID=8YFLogxK
U2 - 10.1021/acs.iecr.6b00378
DO - 10.1021/acs.iecr.6b00378
M3 - Article
AN - SCOPUS:84968791875
SN - 0888-5885
VL - 55
SP - 5116
EP - 5124
JO - Industrial and Engineering Chemistry Research
JF - Industrial and Engineering Chemistry Research
IS - 17
ER -